Wpm 415 C Crystalline Capillary Waterproofing Equ.
CCF179
1
Equ.To Master Flex 801-Based On Pud Resin:
CCF180
1
Part-A
Preparation Of Waterborne Dispersion.
2
Part-B
Hardener On Powder Use Melamine Powder Basf
3
Part-C
Accelerator In Liquid Form
Mix Ratio: Pt-A 20kg + Pt-B 66 Kg + Pt-C 2 Kg.
2
Equ.To Master Flex 801-Based On Vinyl Resin Vach & Vmch
CCF181
1
Part-A
Preparation Of Vinyl Resin Solution
2
Part-B
Hardener In Powder Form Use Melamine Powder Basf
3
Part-C
Accelerator In Liquid Form
Preparation Of Accelerator
Mix Ratio: Pt-A 20 Kg+Pt-B 66 Kg+Pt-C 2kg
3
Preparation Of Resin Composition For Master Flex 801 Based On Pud + Acrylic.
CCF182
Part-A
Preparation Of Pud + Acrylic Solution.
Part-B
Hardener In Powder Form
Part-C
Accelerator In Liquid Form
Mix Ratio: Pt-A 20 Kg + Pt-B 66 Kg + Pt-C 2 Kg.
4
Preparation Of Paver Lacquer:
CCF183
Stage-A Preparation Of Sbr Emulsion
Stage-B Preparation Of Styrene Acrylic Emulsion
Final Mix: 60 Kg Of Stage-A + 40 Kg Of Stage-B
Or 40 Kg Of Pure Acrylic Stage-B
5
Preparation Of Pce Based Chemicals For Different Application:
Formula-1 Preparation Of Spl Additive
CCF184
Formula-A Rmc System Of Pce Based (High Water Reducing Efficiency,
High Compressive Strength,Slump Retaining Ability For 2 Hrs.)
Mix Material: 47.675 Kg Of Formula-A + 40 Kg Of Special Additive+12.325kg Of Water.
6
For Workability Of Concrete Upto 3 Hrs In Hot Weather Condition
With 3 Hrs Of Slump Resistant.
Formula-1 Preparation Of Spl Additive
CCF185
Formula-B
7
Formula-1:Cheaper Pce Based Superplasticiser
CCF186
Mftd.In 3 Stages & Finally Mix Stage 1+2+3 Under Hss For 15 Mints.
8
Formula-2: Cheaper Pce Based Superplasticiser
CCF187
Mftd.In 3 Stages & Finally Mix Stage 1+2+3 Under Hss For 15 Mints.
9
Pce Based Plasticizer: Prepared In 3 Stages Mix Stage 1&Stage 2 Under Hss For 30 Mints & Keep The Mixed Material O/N. Next Day Add 100 Gms Of 9.5 Mole Np And Mix It For 30 Mints And Use.
CCF188
10
Hardeners For Paver Blocks:
Formula-1 Cheaper & Simple Pb Hardener Clear
CCF189
11
Special Hardener For Paver Blocks:
CCF190
12
Chemicals For Paver & Hollow Blocks
CCF191
Preparation Under 3 Stages. Finally Mix 1+2+3 Under Hss
Use 200 - 250 Ml For 50 Kg Cement.
13
Preparation Of Pud White Coat
CCF192
14
Preparation Of Elastomeric Coat
CCF193
15
Pud Complexed With Elastomeric Acrylic Resin For Water Proofing
CCF194
WATER RETARDER:
SL No.
Product Name
Ref No
Enquiry
1
Formula-1
CCF 195
2
Formula-2
CCF 196
Tile Adhesive:
1
Formula-1: Cement Based Tile Adhesives
CCF 197
2
Formula-2
CCF 198
3
Formula-3: Ceramic Tile Adhesives
CCF 199
4
Formula -4
CCF 200
Construction Chemicals Extra:
1
Cementitious Patching & Repair Mortar
CCF 201
2
Cementitious Resurfacing & Underlaying Mortar
CCF 202
3
Cementitious Stucco Formulations
CCF 203
4
Decorative Cementitious SprayCoating White
CCF 204
5
Decorative Cementitious Basement Water Proofing
CCF 205
6
Cement Additive Equ To Dr Fixit Tonic:
Part-A
Preparation Of Cement Additive A,B
CCF 206
Part-B
Integral Wp. Compd.Equ. To Kemproof Iwc And Pidiproof
L.W.
CCF 207
Actual Formulation Take Part-B 80 Kg + Add Part-A 20kg
CCF 208
7
Dr.Fixit Super Latex:
CCF 209
8
High Strength Repair Mortar And Bonding Agent
CCF 210
Sbr Protects Steel From Corrosion. Highly Effective In Water
Proofing And Tank Basements.Also Used In Concrete& Floor
2 Pack System Solventless Pu ClearFor Injection Grout Base.
CCF 244-1
Hardener For Pu Clear (Mix Ratio 5:1 By Wt. Or 3:1 By Wt)
CCF 244-2
Formula-2
11
2 Pack System Epoxy Based Injection Grout- Base
CCF 245-1
Hardener For Epoxygrout Base(Mix Ratio 2:1by Wt)
CCF 245-2
High Quality Cement Polymer Modified Grouting Compound.
12
Formula-1
CCF 246
13
Formula-2
CCF 247
15
Formula-3 (Ec0nomical Quality)
CCF 248
Process: All Raw Materials To Be Charged In Small Ball Or Pot Mill
With Ceramic Balls 10-15 Mm Size As Grinding Media For 45minutes.
15
Admixtures For Rmc System UsingPolycarboxylate Ether Slump Retention > 180 Minutes Extend Workability To3hrs Ideal In Very Hot Weather Conditions.
CCF 249
16
Admixtures For Rmc System UsingUniversal Polycarboxy late Polymer. Slump Retention 60 Minutes
CCF 250
Product Formulation Equ.Pidilite Cc (Dr.Fixit Type Products)
1
Formula-1 Equ. Dr.Fixit Raincoat.
CCF 251
1st Stage: Grinding 53 Kg
2nd Stage: Let Down 48.37 Kg
2
Formula-: Equ Dr.Fixit Aluminium Coat
CCF 252
1st Stage: Leafing Aluminium Paste Soln. 30 Kg
2nd Stage: Bitumen Soln.
Mix Stage 1 And Stage 2 For 3o Mints Under Stirrer.
3
Equ. Pidilite Cc Formulations (Dr.Fixit):
Formula-1 Additive X
CCF 253
4
Formula-2 Equ. Dr. Fixit RepellinWr
CCF 254
5
Formula-3 Equ. Dr.FixitTorchshield Primer Stage-1 Prepn. Of Bitumen Soln. 50 Kg Stage-2 Prepn. Of Chain Stop AlkydPrimer Base. 50.40kg Mix 50 Kg Of Stage-1 And 50 Kg Of Stage-2
CCF 255
6
Gypsum Based Spray Plaster
CCF 256
Self Levelling Floor Coating System:
Formula-A
1
Clear Primer Coat -2 Pack System (Base + Hardener)
CCF 257
Formula-B
2
Top Coat Free Flowing Chem.ResistHigh Gloss With Flooring Upto 3mm Thickness (Base + Hardener)
CCF258
Formula-C
3
Solvent Free Equ. Berger Paints(Base+Hardener)
CCF259
4
Slf Equ. Sika Industries(Base+Hardener)
CCF260
Self-Levelling Floor Coatings & Normal Floor Coatings:
Formula 1.
5
Equ. To Sika Industries (Base+Hardener) Based On Der 353 ResinAnd Cycloaliphatic Epoxy Amine
CCF 261
Formula 2.
6
Equ. To Niti Floor Fc
CCF 262
Formula 3.
7
Equ. Floor Top Sl (Normal Floor Coating) Base + Hardener
Manganese Dioxide Cured 2 Pack Polysulphide Sealant Non Saq
CCF 278
1
Part-1
Based On Liquid Polysulphide
2
Part-2
Based On Manganese Dioxide & Plasticiser
Epoxy Polysulphide Lacquer/Sealant
CCF 279
1
Part-1 Base (Based On Unmodified Epoxy Resin)
2
Part-2 Hardener (Based OnPolysulphide Resin Lp-3 Mol.Wt.1000) Pu Tile Grout:
CCF 280A & CCF 280B
Formula-1 Based On Pu Resin 5:1
Hardner Desmodur Vl
Mix Ratio 5:1 By Wt
Formula-3
Special Epoxy Tile Grout+Tile Fillers 3 Pack System Base 14.5 Kg + Hardner 10 Kg + Filler Compd 14.5 Kg Mix Base + Hardner + Filler In The Ratio Of 4:2:4 Conbextra Ep 10: Two Comp. Low Viscosity Epoxy Resin Injection Grout.
CCF 281
Base : Based On Lapox And Replacure Resin
CCF 282
Hardner: Based On Replamide
Base & Hardner Ratio=77: 23 By Wt
1
Ci For Concrete Based On Textamine
CCF 283
2
Ci For Concrete Powder Form. Formula-1 Based On Zinc Oxide &Molybdate
CCF 284
3
Ci For Concrete Powder Form Formula-2 Calcium Nitrite
CCF 285
4
Liquid Ci For Concrete Formula-1 Based On Amine Carboxylate Solution
CCF 286
5
Liquid Ci Formula-2 Based On Hedp
CCF 287
6
Liquid Ci Formula-3 Based On ZincPhosphate
CCF 288
7
Ci For Concrete Polymer Based
CCF 289
8
Equ.Conplast Nc Accelerator Cum Ci For Concrete Formula-A 1st Stage + 2ndStage
CCF 290
9
Ci For Concrete Liquid Mix Sodium & Calcium Nitrite In Water To MakeUp 100kg
CCF 291
10
Highly Effective Superior Finish Coating On Damp Surfaces Like
Concrete,Rcc,Floor Etc.
Using Epoxy Resin Lapox 101
Part-1 Golden Yellow
CCF 292-1
Part-1 Black
CCF 292-2
Part-1 White
CCF 292-3
Part-2 For Golden Yellow,Black,White Based On Synpol 105x
Part-3 For Golden Yellow,Black,White Based On Water
Mix Pt-1 & Pt-2 And Add Water Tp Pt-3
11
Dampguard Coating Based On Special Epoxy Resin With Anquamine 401 CuringAgent:
Part A Based On Antisol Ep
CCF 293
Part B Based On Anquamine CuringAgent
Part C Based On Water
Mix Ratio: Pt-A, Pt-B, & Pt-C Under Hss
12
W.T. Epoxy Primer
CCF 294
Pt-1 Based On Synpol 130 Grade Resin
Pt-2 Based On Lapox B-11
13
Wt Epoxy White & Orange
CCF 295
Pt-A Base White / Orange Based On Epikote 828
Pt-B Curing Agent Based On Anquamine
CCF 297
Pt-C Water (Mix Part-A+Part-B+ Part-C)
Construction Chemicals:
1
Formula-1 Crystalline Formulation Water Proofing(Xylex)
CCF 296
2
Formula-2 Crystalline Powder Form Equ. Penitron Usa
CCF 297
Above Formulation To Make Concrete As A Crystalline Base PenetratingConcrete In This Micro Crystal Form In Concrete & Reduce Total PorosityIn Case Of Water Is In Contactwith This, Concrete Micro Crystal Activate& Again Reduce The Porosity With Densify The Concrete.
Dosage: 300 Gms Per Bag Of Cement 50 Kg
3
FORMULA-2B IN THE ABOVE FORMULATION ADDITION OF TARTARIC ACID + GLUCONICACID TO BE ADDED. EQU.STUDGUARD GERMAN FORMULA.